3240 EPOXY PHENOLIC GLASS CLOTH LAMINATED SHEET

IT CONSIST OF SUPERIMPOSED LAYERS OF ALKALIFREE E-GLASS CLOTH THAT HAVE BEEN SUBSTANTIALLY IMPREGNATED WITH EPOXY AND PHENOLIC RESINS AND BONDED TOGETHER UNDER PRESSURE WITH HEAT TO FORM A SINGLE PIECE. IT HAVE HIGH MECHANICAL PROPERTIES, CAN BE USED IN ELECTRICAL MACHINERIES AND DEVICES AS INSULATING CONSTRUCTION PARTS AND IN MOIST CICUMSTANCES AND IN TRANSFORMER OIL.

DENSITY: 1.70-1.90g/cm3
TENSILE STRENGTH: 300Mpa
SIZE: 1.0MM-80MM(THICK) X1000MM(WIDTH)X2000MM(LENGTH)
epoxy phenolic glass cloth laminated sheets

IT CONSISTS OF COTTON CLOTH, WHICH HAS BEEN IMPREGNATED WITH PHENOLIC RESIN, DIRED, CURED IN MOULD UNDER PRESSURE WITH HEAT MACHINED TO FORM A SINGLE PIECE. THE PRODUCT HAS HIGHER MECHANICAL PROPERTIES AND MACHINABILITY CAN BE USED AS INSULATION CONSTRUCTION PARTS IN ELECTRIC MACHINE AND DEVICE, AND USED IN TRANSFORMER OIL.

DENSITY: 1.25-1.40g/cm3
TENSILE STRENGTH: 80.0Mpa
DIA. 6MM-100MM, LENGTH: 1000MM
phenolic laminated cotton cloth rods

IT CONSISTS OF ALKALIFREE E-GLASS CLOTH THAT HAVE BEEN IMPREGNATED WITH EPOXY AND PHENOLIC RESINS, DRIED, CURED IN MOULD UNDER PRESSURE WITH HEAT TO FORM A SINGLE PIECE. IT HAVE HIGH MECHANICAL PROPERTIES, CAN BE USED IN ELECTRICAL

DENSITY: 1.70-1.90 g/cm3
TENSILE STRENGTH: 196Mpa
DIAL: 6MM-100MM, LENGTH: 1000MM
epoxy phenolic laminated glass cloth rods